Improvement of mechanical property and corrosion resistance of Mg-Zn-Nd alloy by bi-direction drawing

Mg-Zn-Nd alloy is a promising biodegradable metal material for surgical staples during the reconstruc-tion of digestive tract due to its good biocompatibility and suitable mechanical properties.However,its deformation property and corrosion resistance should be improved to make better safety and effective-ness of staples.In the present study,bi-direction drawing was adopted to maintain the initial texture characteristics,and improve mechanical property and corrosion resistance of Mg-2Zn-0.5Nd alloy.The results showed that the microstructure after bi-direction did not change too much,but the texture could maintain its initial characteristics.The ductility of the alloy with 60 ％ accumulative area reduction after bi-direction drawing was increased by 70 ％,indicating that an outstanding deformation property of Mg-Zn-Nd alloy can be obtained by bi-direction drawing.The corrosion resistance was also improved after bi-direction drawing compared with that under single direction drawing.     

退火工艺对激光选区熔化成形Ti6Al4V合金组织及室温力学性能的影响

以Ti6Al4V球形粉末为原料,利用激光选区熔化成形方法制备了Ti6Al4V合金试样,采用光学显微镜、扫描电镜及力学性能测试等手段,研究了退火工艺对Ti6Al4V合金室温力学性能及组织的影响规律。结果表明: SLM成形沉积态Ti6Al4V合金室温抗拉强度超过1200 MPa,而平均断后伸长率仅为4.0%;在650 ℃下进行真空退火处理,合金的抗拉强度仍保持在1200 MPa左右,规定塑性延伸强度R_p0.2高于1150 MPa,但试样的断后伸长率<10%;而在750及800 ℃下进行真空退火处理,合金试样的抗拉强度降至1100 MPa左右,规定塑性延伸强度高于1050 MPa,伸长率达到甚至超过10%,材料的综合强韧性得到明显提升。随着真空退火加热温度和保温时间的增加,SLM成形Ti6Al4V合金原始β晶界逐渐变模糊,晶粒趋向于等轴化。与此同时,快速冷却转变的α′针状马氏体未出现明显地粗化。     

基于知识图谱和协同过滤的电影推荐算法研究

针对协同过滤算法在推荐电影过程中只能考虑电影外部评论而不能考虑电影内部的相似度关系,提出构建知识图谱辅助计算电影内部相似度。已有的电影数据可能是不完整的,因此采用知识图谱推理补全缺失的电影知识。基于TransE模型的知识图谱无法有效描述电影间的片名、演员、导演等复杂的多关系。首先采用改进的TransHR模型表示出电影信息之间的多关系,提升关系表示的准确率;然后通过用户评分矩阵计算电影间相似度;最后将2种相似度融合并应用于矩阵分解的推荐技术中。对比实验结果表明,该算法在召回率、准确率、平均绝对误差MAE等指标上都有所提升。     

无线电综合测试仪校准装置的研究及其不确定度分析

This calibration device of radio comprehensive tester is studied and established in this paper. It solves the verification and calibration of a large number of general-purpose radio comprehensive testers. The calibration device consists of four calibration sub- systems and calibration software system, including RF generator, audio generator, audio analyzer and RF analyzer. It also researches on the configuration of standard equipment and analyzes the uncertainty of the calibration devices, ensuring accurate and reliable val- ue transfer.     

Fabrication of Cu/graphite film/Cu sandwich composites with ultrahigh thermal conductivity for thermal management applications

Effective thermal management of electronic integrated devices with high powder density has become a serious issue, which requires materials with high thermal conductivity (TC). In order to solve the problem of weak bonding between graphite and Cu, a novel Cu/graphite film/Cu sandwich composite (Cu/GF/Cu composite) with ultrahigh TC was fabricated by electro-deposition. The micro-riveting structure was introduced to enhance the bonding strength between graphite film and deposited Cu layers by preparing a rectangular array of micro-holes on the graphite film before electro-deposition. TC and mechanical properties of the composites with different graphite volume fractions and current densities were investigated. The results showed that the TC enhancement generated by the micro-riveting structure for Cu/GF/Cu composites at low graphite content was more effective than that at high graphite content, and the strong texture orientation of deposited Cu resulted in high TC. Under the optimizing preparing condition, the highest in-plane TC reached 824.3 W·m⁻¹·K⁻¹, while the ultimate tensile strength of this composite was about four times higher than that of the graphite film.     

单晶SiC的电助光催化抛光及去除机理

为满足电子半导体等领域对SiC超光滑、无损伤和材料高效去除的要求，提出了电助光催化抛光SiC的新方法。研究了光催化剂种类及其pH值对抛光液氧化性和抛光效果的影响，讨论了材料的去除机理。结果表明：以p25型TiO2为光催化剂配制抛光液所获得的最大氧化还原电位为633.11 mV，材料去除率为1.18 μm/h，表面粗糙度Ra=0.218 nm；抛光后SiC表面氧化产物中，Si-C-O、Si-O和Si4C4O4的含量明显增加，SiC表面被氧化并被机械去除是主要的材料去除方式。     

高强不锈钢绞线网与ECC黏结-滑移关系模型

高强不锈钢绞线网与ECC的黏结是二者协同工作的基础，且黏结 滑移关系模型是其黏结性能的综合反映，故通过对17组51个高强不锈钢绞网增强ECC薄板试件进行单边拉拔试验，研究横向钢绞线间距、纵向钢绞线直径和相对锚固长度等因素对钢绞线网在ECC中黏结性能的影响规律。试验结果表明，横向钢绞线的设置可使黏结破坏由脆性破坏转变为延性破坏；高强不锈钢绞线网与ECC的黏结滑移曲线可分为5个阶段，分别为上升段、微降段、延性强化段、下降段和残余段。基于试验结果，对钢绞线网在ECC中的黏结破坏特征和黏结 滑移机理进行分析，在相关黏结-滑移关系模型的基础上，提出钢绞线网与ECC的黏结 滑移关系模型，并进行模型参数分析。所提模型及模型参数计算公式与试验结果吻合良好，能较好地反映钢绞线网与ECC的界面黏结滑移特征。